Finite Element Analysis of Mechanical Properties of Graded Sphere Porosity Structure with Different Pore Size Distributions
Shi Zhiliang1, Huang Chen1, Lu Xiaolong1, Li Feng2*, Sun Yunlong2
1(School of Mechanical and Electrical Engineering, Wuhan University of Technology, Wuhan 430070, China); 2(Tongji Medical College, Huazhong University of Science & Technology, Wuhan 430030, China)
Abstract：To establish a three-dimensional finite element model of titanium alloy porous structure with the different pore size distributions and to implement the finite element mechanical analysis. The sphere, sphere_line, sphere_plane, sphere_point three-dimensional models of porous structure was created by software Rhino 5.0. The finite element analysis was implemented by Abaqus 6.1 to calculate the Von-Mises stress and maximum principal stress. Before calculated, The 200, 400, 600, 800, and 1000 N loading forces were applied to the upper surface, and the direction was vertically downward. The lower surface was selected as a fixed constraint. Under the same loading force, thesphere plane has the maximum principal stress and the maximum equivalent stress,followed were the sphere point gradient pore model and sphere line gradient pore model, the sphere without gradient pore model was the smallest. Among the four porous structures with different gradient pore size distributions, sphere has the lowest actual load and the best carrying capacity, the next was sphere line gradient hole structure and then sphere point. Sphere plane gradient pore structure had the maximum actual load, and its carrying capacity was worse than the three formers. Finally, the four models that were designed in this work were prepared by rapid prototyping to obtain the porous titanium alloy body, and the mechanical property test on these bodies was carried out. The conclusion verifies the reliability of numerical simulation results. The results of this research could be used to provide relevant reference and theoretical basis for porous titanium alloy implants and clinical applications.
石志良, 黄琛, 卢小龙, 李锋, 孙允龙. Sphere梯度孔结构力学性能有限元分析[J]. 中国生物医学工程学报, 2019, 38(3): 339-347.
Shi Zhiliang, Huang Chen, Lu Xiaolong, Li Feng, Sun Yunlong. Finite Element Analysis of Mechanical Properties of Graded Sphere Porosity Structure with Different Pore Size Distributions. Chinese Journal of Biomedical Engineering, 2019, 38(3): 339-347.
[1] 周梦, 成艳, 周晓晨,等. 基于增材制造技术的钛合金医用植入物[J]. 中国科学:技术科学, 2016, 46(11):1097-1097. [2] Niinomi M. Mechanical biocompatibilities of titanium alloys for biomedical applications[J]. Journal of the Mechanical Behavior of Biomedical Materials, 2008, 1(1):30-42. [3] 戚留举, 李子夫, 张春雨,等. 基于选择性激光熔化制备多孔钛结构的设计及分析[J]. 机械, 2014(5):70-74. [4] Bose S, Roy M, Bandyopadhyay A. Recent advances in bone tissue engineering scaffolds[J]. Trends in Biotechnology, 2012, 30(10):546-549. [5] Banhart J. Manufacture, characterisation and application of cellular metals and metal foams[J]. Progress in Materials Science, 2001, 46(6):559-632. [6] Semlitsch MF, Weber H, Streicher RM, et al. Joint replacement components made of hot-forged and surface-treated Ti-6Al-7Nb alloy[J]. Biomaterials, 1992, 13(11):781-788. [7] Arabnejad S, Burnett JR, Pura JA, et al. High-strength porous biomaterials for bone replacement: A strategy to assess the interplay between cell morphology, mechanical properties, bone ingrowth and manufacturing constraints[J]. Acta Biomaterialia, 2016, 30(8):345-356. [8] Seah KHW, Thampuran R, Teoh SH. The influence of pore morphology on corrosion[J]. Corrosion Science, 1998, 40(4-5):547-556. [9] Cansizoglu O, Harrysson O, Cormier D, et al. Properties of Ti-6Al-4V non-stochastic lattice structures fabricated via electron beam melting[J]. Materials Science & Engineering A, 2008, 492(1-2):468-474. [10] Sun W, Starly B, Darling A, et al. Computer-aided tissue engineering: application to biomimetic modelling and design of tissue scaffolds[J]. Journal of Medical Biomechanics, 2004, 39(1):49-58. [11] Attar H, Calin M, Zhang LC, et al. Manufacture by selective laser melting and mechanical behavior of commercially pure titanium[J]. Materials Science & Engineering A, 2014, 593(2):170-177. [12] 邓珍波, 周长春, 樊渝江,等. 多孔钛骨组织工程支架设计及孔结构表征[J]. 稀有金属材料与工程, 2016(9):2287-2292. [13] Geetha M, Singh AK, Asokamani R, et al. Ti based biomaterials, the ultimate choice for orthopaedic implants-A review[J]. Progress in Materials Science, 2009, 54(3):397-425. [14] Boccaccio A, Uva AE, Fiorentino M, et al. Geometry design optimization of functionally graded scaffolds for bone tissue engineering: A mechanobiological approach[J]. PLoS ONE, 2016, 11(1):e0146935. [15] Zhou C, Xie P, Chen Y, et al. Synthesis, sintering and characterization of porous nano-structured CaP bioceramics prepared by a two-step sintering method[J]. Ceramics International, 2015, 41(3):4696-4705. [16] Zhou CC, Ye XJ, Fan YJ, et al. Synthesis and characterization of CaP/Col composite scaffolds for load-bearing bone tissue engineering[J]. Composites Part B, 2014, 62(5):242-248. [17] Zhou C, Ye X, Fan Y, et al. Biomimetic fabrication of a three-level hierarchical calcium phosphate/collagen/hydroxyapatite scaffold for bone tissue engineering.[J]. Biofabrication, 2014, 6(3):035013. [18] Nielsen LF. Elasticity and damping of porous materials and impregnated materials[J]. Journal of the American Ceramic Society, 2010, 67(2):93-98. [19] 黄伯云. 有色金属材料手册[M]. 北京: 化学工业出版社, 2009:585-593. [20] 刁颖敏. 生物力学的原理与应用[M]. 上海:同济大学出版社, 1991:216-218.